Magnetisation Grade: N45H
Material: Neodymium-Iron-Boron (NdFeB)
Magnet ID: NRD-612-N45H
Plating / Coating: Nickel (Ni-Cu-Ni) / Double Ni / Zinc (Zn) / Epoxy (Black/Gray) / Gold (Au)
Shape: Rod, Cylinder, Bar
Rod Magnet Size:
Rod Total Diameter (D): 6 mm
Rod Total Height (H): 12 mm
Tolerance: ±0.05 mm
Magnetisation Direction: Axial / Radial
Residual Magnetic Flux Density (Br): 1320-1380 mT (13.2-13.8 kGs)
Energy Density (BH)max: 326-358 KJ/m³ (43-46 MGOe)
Coercivity Force (Hcb): ≥ 963 kA/m ( ≥ 12.1 kOe)
Intrinsic Coercivity Force (Hcj): ≥ 1353 kA/m ( ≥ 17 kOe)
Maximum Operation Temperature: 120 °C
Delivery Time: 14-35 days
Sintered Neodym Magnete grade
N35, N38, N40, N42, N45, N48, N50, N52(Max. Operational temperature: 80c)
N35M, N38M, N40M, N42M, N45M, N48M(Max. Operational temperature: 100c)
N35H, N38H, N40H, N42H, N45H, N48H, (Max. Operational temperature: 120C)
N33SH, N35SH, N38SH, N40SH, N42SH(Max. Operational temperature: 150c)
N28UH, N30UH, N33UH, N35UH, N38UH(Max. Operational temperature: Up to 180c)
N28EH, N30EH, N33EH, N35EH(Max. Operational temperature: Up to 200c)
N30AH, N33AH, N35AH(Max. Operational temperature: Up to 230c)
Sintered Neodym Magnet Outsanding product:
1)high performance:N52,N48M,48SH,42UH,38EH,33AH
2)high working temperature:the AH series with 40 k Oe super-high coervice force can replace SmCo magnets successfully.
3)high consistency:the cpk of Br and Hcj are much higher than 1.67 the consisitency of surface magnetic field and magnetic flux can be controlled with +/-1%
4)High Anti-corrosion:the sale spray test and humid heat test of the high anti-corrosion coating could be more than 1000 hours
5) low weight loss
PCT:130c ,humidity 100%,vapor pressure 2.7 bar.20 days,average low weight loss less than 2 mg/cm2